Rust prevention is important for steel structures, as without it, steel will rust over time, depending on the atmospheric conditions of the environment where the structure is used.
Rust is the corrosion product formed when steel reacts with oxygen and water. The rust reaction is generally denoted as follows:
4Fe + 2H2O + 3O2 = 2Fe2O3 H2O
Although rust is primarily hydrated ferric oxide, it also contains other compounds. Rusts have a wide range of composition, depending on the conditions under which they are formed. Typical compositions cannot, therefore, be given but analyses of a range of rusts have indicated that airformed rusts generally contain about 5 % of compounds other than Fe2O3 H2O.
These derive in part from the steel, which contains elements other than iron, e.g. copper, silicon and manganese, and in part from atmospheric contaminants and pollutants, mainly sulphates and chlorides, although other pollutants such as ammonium salts are also generally present in rust.
The constituents formed by reactions between steel and pollutants such as sulphur dioxide, sometimes called ‘iron salts’ or ‘corrosion salts’, cause most problems for coatings applied onto rusting steel surfaces.
Sulphur dioxide in the air reacts with moisture to form acids. Weak sulphuric acid solutions react with the steel to form ferrous sulphate. These salts tend to form in shallow pits at the steel surface and the corrosion process is such that the sulphates tend to move inwards to the anodic areas, which are likely to be in crevices, the bottom of pits, etc.
The salts are also not ‘rust’ coloured, being white or light coloured. They are very difficult, if not impossible, to remove with tools such as scrapers and wire brushes and are often difficult to remove even with blast-cleaning. The presence of salts such as ferrous sulphate leads to rather complex reactions involving the regeneration of the sulphuric acid from which they were formed. This in turn causes further corrosion and the production of more rust (see Figure below). As rust has a considerably greater volume than the steel from which it is produced, this can lead to disruption of any coating applied over it by cracking, blistering and eventually flaking.
Ferrous sulphate is the salt most commonly found in rusts formed in industrial-type atmospheres. Near the coast, chlorides are likely to be a greater problem. The reactions arising from the two types of salt, sulphate and chloride, are not necessarily the same. Chlorides are hygroscopic, i.e. they absorb moisture. It has been shown in laboratory tests5 that whereas rusting may occur at relative humidities below 70% with sulphates, the presence of chlorides in rust can result in corrosion of the steel at relative humidities as low as 40%. Chlorides may, therefore, be a greater immediate problem than sulphates.
How to Prevent Rust
There are many rust prevention methods. An important step within the process is to ensure good surface preparation has taken place before application of the protective system.
- Most popular corrosion prevention processes include the use of paint or metallic coatings
- Within metallic coatings the following processes are generally used:
- hot dip galvanizing
- zinc thermal spraying
- aluminium thermal spraying
Corrosion prevention by galvanizing steel
Galvanizing is an effective corrosion prevention method as when clean steel is immersed into molten zinc, a metallurgical reaction between the iron and zinc creates a series of zinc-iron alloy layers, providing a robust coating which is an integral part of the steel.
Hot dip galvanizing has been used for a very long time to protect steel structures in various environments and it is proven to last between 34 to 170 years. Galvanizing is a great for corrosion protection, as it is cost effective, honest and sustainable.
Our campaign aims to highlight the extensive amount of corroding steelwork across the UK and Ireland.
Protecting steelwork correctly on day one can help to save money spent on replacement or maintenance, which can be much more expensive than the initial cost of protection.
An even more important aspect of correct corrosion protection is the contribution it can make to a more sustainable built environment.
Find out how you can stop rust
Steelwork Corrosion Control- D.A. Bayliss and D.H. Deacon